Brass Wires

We offer a variety of Brass Wire, Brass Flat Wire, Square Brass Wire which are extensively used in automobile, electronic, electric & nipples. Our range of brass wire mesh is acclaimed for its durability, excellent performance and minimal prices.

We also offer various other grades of Brass Wire like Riveting Brass Wire, Forging Grade Brass Wire, Free Cutting Grade, EDM Brass Wire, Lead Free Brass Wire – IS:2074, BS:2874 CZ119, IS:4170/75, CuZn38PB1, Free Cutting – BS249, IS:319 Gr. l & ll, IS:8364 Gr. l & ll, BS:2874 CZ121Pb3, CuZn39Pb3, Lead Free, IS4413, CuZn37, DTD-627, 60:40.

Riveting Brass Wire

  • IS:2074
  • BS:2874CZ119
  • IS:4170/75
  • CuZn 38PB1 / 1.5
  • CZ129

Chemical Requirements

CZ119 CZ129
CuZn37Pb2 CuZn38Pb1
Copper 61.0 – 64.0% 59.0 – 62.0%
Lead 1.0 – 2.50% 0.80 -1.50%
Iron 0.15%max 0.15%max
Total Imp. 0.30% 0.50%
Zinc Reminder Reminder
Physical Properties CZ119 CZ129
Condition T.S. MPA EL % Min T.S. MPA EL % Min
Manufacturing 350-380 22 350-380 25
Fabrication Properties CZ119 CZ129
Capacity for being
Cold worked Fair Fair
Hot formed Excellent Excellent
Machinability Rating 80% 80%
Suitability for soldering Fair Excellent
Suitability for Brazing Good Good
 

Application :
Typically used: Fasteners, Rivets, Domestics application, Automotive Engineering
Hose Fittings , Intricate parts such as clock components.

Free Cutting Brass Wire

  • BS249
  • IS:319 Gr. l & ll
  • IS:8364 Gr. l & ll
  • BS:2874 CZ121Pb3
  • CuZn39Pb3
Chemical Requirements Grade I Grade II Grade III
Copper 56.0 – 59.0% 60.0 – 63.0% 60.0 – 63.0%
Lead 2.0 to 3.50% 2.50 – 3.70% 0.50 – 1.50%
Iron 0.35% max 0.35% max 0.20% max
Total Imp. Excl. Iron 0.70% max 0.50% max 0.50% max
Zinc Remainder Remainder Remainder
Physical Properties Grade I Grade II Grade III
Condition Size T.S. MPA EL% Min T.S. MPA EL% Min T.S. MPA EL% Min
Annealed (O) 6-25
25-50
50 above		 345
315
285		 12
17
22		 355
305
275		 15
20
25		 315
285
255		 22
27
32
Half-Hard (HB) 6-12
12-25
25-50
50 above		 405
395
355
325		 4
6
12
17		 395
385
345
315		 7
10
15
20		 355
345
305
285		 8
12
22
27
Hard (HD) 6-12
12-25		 550
485		 –
4		 550
485		 –
4		 460
400		 –
4
Fabrication Properties Grade I Grade II Grade III
Capacity for being
Cold worked Poor Poor Poor
Hot formed Fair Fair Fair
Machinability Rating 100% 90% 90%
Suitability for soldering Excellent Excellent Excellent
Suitability for Brazing Good Good Good
Uses
Precision Components, Hardware, Hinges, Lock Bodies, Screws, Nuts & Bolts
Gr II : Gear, Pinions, Precision, Automobile, Electronic Parts
Gr III : Precision Components Machining with Riveting Operation

 

Lead Free Brass Wire

We are one of the leading manufacturer and suppliers of Lead-Free Brass Wire with the using of the high quality of material, as per the industry standards.

  • IS4413
  • CuZn37
  • DTD-627
  • 60:40 Brass

 

Chemical Requirements CuZn40 CuZn35 CuZn37 CuZn30
Copper 59.0 – 62.0% 63.0 – 68.5% 62.0 – 65.0% 60.5 – 71.50%
Lead 0.75% max 0.05% max 0.30% max. 0.05% max.
Iron 0.10% max 0.05% max 0.10% max 0.05% max.
Total Imp. 0.30% max 0.30% max 0.60% max 0.30% max
Zinc Remainder Remainder Remainder Remainder

Physical Properties

Condition T.S. MPa EL% Min T.S. MPa EL% Min
Annealed (O) 325 Min 35% 315 Min 45%
Half-Hard (HB) 460-620 – 460-620 –
Hard (HD) 660-775 – 620 min –

Fabrication Properties

Capacity for being
Cold forming Excellent
Machinability Rating 40%
Bending Excellent
Riveting Excellent
Forging Excellent
Uses
Suitable for cold Heading, Forging, End Pressing & Bending

 

Specialized Brass Wires

Meeting the demands of our clients, we are engaged in offering quality range of Specialized Brass Wires that are available in varied sizes. Manufactured in compliance with industrial standards these wires have gained wide appreciation for superior strength and durability.

 

Brass Brazing Wire

We are one of the leading manufacturer and suppliers of Brass Brazing Wire with the using of a high quality of material, As per the industry standards.

Equivalent Specification

  • DIN 8513
  • EN 1044
  • ISO 17672 ( 2010-11)
  • Aws A5.8.89

Product Details:

  • Material : Brass Brazing
  • Diameter : 2-2.5 mm, 0-0.5 mm, 1.5-2 mm, 0.5-1 mm, >2.5 mm, 1-1.5 mm
  • Gauge : 26 SWG, 22 SWG, 18 SWG
  • Composition (Tin/Lead) : 60/40, 63/67
  • Thikness : 0.1-6

Chemical Requirements

L-CuZn40 Mn2
Copper 60 60
Zinc 39.7 39.7
Silicon 0.3 0.3
Mn – 0.2
Uses
Use for brass brazing ,steels malleable cast iron, copper,
copper alloy with melting temperatures greater than 950°C (Solidous), nickel, nickel alloys.
Mn2 Use for copper, cast and malleable iron brazing.

 

 

Brass Wire for Ball Pen Tip

The entire range of Brass Wire for Leaded Ball Pen Tip is manufactured using finest quality of brass procured from reliable and certified sources of the market. These wires are valued for their resistivity against thermal conductivity, longer operational life, low maintenance and strength. We also specialize in field of customization to offer complete client satisfaction. These are manufactured in compliance with industrial standards and finds application in various sectors.

Chemical Requirements
Copper 56.0 – 59.0%
Lead 2.5 to 3.50%
Iron 0.05% max
Zinc Remainder
Total Imp. 0.35% max
Physical Properties
Size (mm) T.S.Kg/mm2 EL% Min
1.60 mm R 50 – 60 6 – 10%
1.98 mm R 50 – 60 6 – 10%
2.25 mm R 50 – 60 6 – 10%
2.30 mm R 50 – 60 6 – 10%
2.70 mm R 50 – 60 6 – 10%
Fabrication Properties
Capacity for being
Cold Heading Fair
Machinability 100%
Plating Good
Uses
Ball Pens Industries for Writing Pens

Nickel Silver Wires for Ball Pen Tips

Nickel silver wire is a copper alloy with nickel & sometimes with zinc as well. It is known to have a composition of 60% Copper, 20% nickel and 20% Zinc. We offer a premium quality range of Nickel Silver Wire for Ball Pen Tip, which is acknowledged for its resistance corrosion, high strength and high conductivity. Due to our high-powered conductivity and Eddey current tests, we have been able to fabricate and export defect less range of nickel plated wire.

Specifications:

  • Material: Nickel Silver
  • Colour: Silver
  • Thickness: 0.2.5-7 mm

 

Chemical Requirements
Copper 42.0 – 47.0%
Lead 1.0 to 2.2%
Iron 0.30% max
Nickel 9.0 to 12.0%
Manganese 4.0 to 7.0%
Zinc Remainder
Total Imp. 0.30% max
 

Physical Properties
Size (mm) T.S.Kg/mm2 EL% Min
1.20 mm R 65 – 75 6 – 15%
1.60 mm R 65 – 75 6 – 15%
1.98 mm R 65 – 75 6 – 15%
2.30 mm R 70 – 80 6 – 15%
2.50 mm R 70 – 80 6 – 15%
 

Fabrication Properties
Capacity for being
Cold Heading Fair
Machinability 80%
Plating Not Require
Uses
Ball Pens Industries for Writing Pens

 

Brass Zipper Wires

We provide High Quality Brass flat Wire with Bright surface finishing and brass colour,widely uses in Zipper Industries suitable for teeth formation ,bending and punching work, top and bottam stopper. And suitable for electronic industries for punching work

Equivalent Specification
Germany DIN Europe EN Inter.StandardOrg.ISO USA UNS Japan JIS France NS United Kingdom BS
CuZn37 CuZn37 CuZn37 C27200 C2720 CuZn37 CZ108
CuZn30 CuZn30 CuZn30 C26000 C2600 CuZn30 CZ106

Chemical Composition

 CuZn37 CuZn30
Copper 62-64% 68-71%
Lead 40 ppm (max) 40 ppm (max)
Iron 100 ppm (max) 100 ppm (max)
Zinc Rem Rem
Impurities 0.2 Max 0.2 Max

Size: Available

Min Max Tolerence
Width: 2.5 mm 10 mm +/-0.03 mm
Thickness 0.80mm 2.00mm +/-0.02mm
Hardness 90 HV 170HV
Coil Weight 30-50 Kgs
Coil I.D. 300 mm
Coil Width 100 mm

 

Brass Brazing Rods

Copper alloys are base metal alloys used for high temperature brazing of steels or tungsten carbide. Cost effective alternative to silver brazing alloys wherein high joint strength can be readily achieved. Some alloys also offer excellent corrosin resistance with thermal and electrical conductivity. we offer these alloys in standard composition to suitable specific application available in wires and rods.

GermanyDIN Europe EN Inter.StandardOrg.ISO Aws
Din:8513 En1044 17672(2010-11) A5.8.89

 

Chemical Composition L-CuZn40 Mn2
Copper 60 60
Zinc 39.7 39.7
Silicon 0.3 0.3
Mn – 0.2
Uses
Use for brass brazing ,steels malleable cast iron, copper,
copper alloy with melting temperatures greater than 950°C (Solidous), nickel, nickel alloys.
Mn2 Use for copper, cast and malleable iron brazing.

 

Brass Flat Wire

We provide High Quality Brass flat Wire with Bright surface finishing and brass colour,widely uses in Zipper Industries suitable for teeth formation ,bending and punching work, top and bottam stopper.

And suitable for electronic industries for punching work.

Equivalent Specification
Germany DIN Europe EN Inter.StandardOrg.ISO USA UNS Japan JIS France NS United Kingdom BS
CuZn37 CuZn37 CuZn37 C27200 C2720 CuZn37 CZ108
CuZn30 CuZn30 CuZn30 C26000 C2600 CuZn30 CZ106

Chemical Composition

CuZn37 CuZn30
Copper 62-64% 68-71%
Lead 40 ppm (max) 40 ppm (max)
Iron 100 ppm (max) 100 ppm (max)
Zinc Rem Rem
Impurities 0.2 Max 0.2 Max

 

Size: Available
Min Max Tolerence
Width: 2.5 mm 10 mm +/-0.03 mm
Thickness 0.80mm 2.00mm +/-0.02mm
Hardness 90 HV 170HV
Coil Weight 30-50 Kgs
Coil I.D. 300 mm
Coil Width 100 mm